We report about the synthesis and characterisation of two NiCeZrO2 catalysts prepared by one pot-coprecipitation method. The two samples are characterised by similar chemical composition (15 wt% Ni, Ce/Zr = 80/20 atomic ratio) and properties of the CeZrO2 support, which is a cubic phase solid solution with nanometer sized (5–6 nm) crystalline hexagonal/roundish particles. The main differences between the samples are in the NiO particles dispersion and surface area, which were found to be affected by the synthesis pH. Both samples were characterised about their surface properties by employing FTIR spectroscopy of adsorbed CO probe, and tested about their activity and stability in methane steam reforming (MSR) reaction at relatively low temperature (793 K). The results show a good activity in MSR irrespective of the NiO size and morphology, with negligible CO formation, but a strong dependence of the catalysts stability upon these parameters. Only the catalyst with smaller (5–10 nm) NiO particles was found stable for 250 h in MSR at relatively high steam to carbon ratio (S/C = 2). This performance could be related to a positive effect of the CeZrO2 support, allowing fast and easy oxygen transfer to and from the NiO/Ni0 active phase, most likely thanks to the occurrence of a strong metal–support interaction.

Unravelling the structure and reactivity of supported Ni particles in Ni-CeZrO2 catalysts

MILETTO, IVANA;COLUCCIA, Salvatore;BERLIER, Gloria
2013-01-01

Abstract

We report about the synthesis and characterisation of two NiCeZrO2 catalysts prepared by one pot-coprecipitation method. The two samples are characterised by similar chemical composition (15 wt% Ni, Ce/Zr = 80/20 atomic ratio) and properties of the CeZrO2 support, which is a cubic phase solid solution with nanometer sized (5–6 nm) crystalline hexagonal/roundish particles. The main differences between the samples are in the NiO particles dispersion and surface area, which were found to be affected by the synthesis pH. Both samples were characterised about their surface properties by employing FTIR spectroscopy of adsorbed CO probe, and tested about their activity and stability in methane steam reforming (MSR) reaction at relatively low temperature (793 K). The results show a good activity in MSR irrespective of the NiO size and morphology, with negligible CO formation, but a strong dependence of the catalysts stability upon these parameters. Only the catalyst with smaller (5–10 nm) NiO particles was found stable for 250 h in MSR at relatively high steam to carbon ratio (S/C = 2). This performance could be related to a positive effect of the CeZrO2 support, allowing fast and easy oxygen transfer to and from the NiO/Ni0 active phase, most likely thanks to the occurrence of a strong metal–support interaction.
2013
138-139
353
361
http://dx.doi.org/10.1016/j.apcatb.2013.02.036
S. Gopalakrishnan; M.G. Faga; I. Miletto; S. Coluccia ;G. Caputo; S. Sau; A. Giaconia; G. Berlier
File in questo prodotto:
File Dimensione Formato  
Appl Catal B 13 OA.pdf

Open Access dal 06/03/2015

Tipo di file: POSTPRINT (VERSIONE FINALE DELL’AUTORE)
Dimensione 1.2 MB
Formato Adobe PDF
1.2 MB Adobe PDF Visualizza/Apri
NiCeZrO Appl Cat B 13.pdf

Accesso riservato

Tipo di file: PDF EDITORIALE
Dimensione 1.79 MB
Formato Adobe PDF
1.79 MB Adobe PDF   Visualizza/Apri   Richiedi una copia

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/2318/132210
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 29
  • ???jsp.display-item.citation.isi??? 26
social impact