Fibrous substrates functioning as temporary extracellular matrices can be prepared easily by electrospinning, yielding fibrous matrices suitable as internal fillers for nerve guidance channels. In this study, gelatin micro- or nano-fibres were prepared by electrospinning by tuning the gelatin concentration and solution flow rate. The effect of gelatin fibre diameter on cell adhesion and proliferation was tested in vitro using explant cultures of Schwann cells (SC) and dorsal root ganglia (DRG). Cell adhesion was assessed by quantifying the cell spreading area, actin cytoskeleton organization and focal adhesion complex formation. Nano-fibres promoted cell spreading and actin cytoskeleton organization, increasing cellular adhesion and the proliferation rate. However, both migration rate and motility, quantified by transwell and time lapse assays respectively, were greater in cells cultured on micro-fibres. Finally, there was more DRG axon outgrowth on micro-fibres. These data suggest that the topography of electrospun gelatin fibres can be adjusted to modulate SC and axon organization and that both nano- and micro-fibres are promising fillers for the design of devices for peripheral nerve repair.

The influence of electrospun fibre size on Schwann cell behaviour and axonal outgrowth

GNAVI, SARA;FORNASARI, BENEDETTA ELENA;ZANETTI, Marco;GEUNA, Stefano
;
PERROTEAU, Isabelle
Last
2015-01-01

Abstract

Fibrous substrates functioning as temporary extracellular matrices can be prepared easily by electrospinning, yielding fibrous matrices suitable as internal fillers for nerve guidance channels. In this study, gelatin micro- or nano-fibres were prepared by electrospinning by tuning the gelatin concentration and solution flow rate. The effect of gelatin fibre diameter on cell adhesion and proliferation was tested in vitro using explant cultures of Schwann cells (SC) and dorsal root ganglia (DRG). Cell adhesion was assessed by quantifying the cell spreading area, actin cytoskeleton organization and focal adhesion complex formation. Nano-fibres promoted cell spreading and actin cytoskeleton organization, increasing cellular adhesion and the proliferation rate. However, both migration rate and motility, quantified by transwell and time lapse assays respectively, were greater in cells cultured on micro-fibres. Finally, there was more DRG axon outgrowth on micro-fibres. These data suggest that the topography of electrospun gelatin fibres can be adjusted to modulate SC and axon organization and that both nano- and micro-fibres are promising fillers for the design of devices for peripheral nerve repair.
2015
48
620
631
Electrospun fibres, Extracellular matrix, Cell adhesion, Cell spreading, Axon outgrowth, Nerve tissue engineering
S. Gnavi; B.E. Fornasari; C. Tonda-Turo; G. Ciardelli; M. Zanetti; S. Geuna; I. Perroteau
File in questo prodotto:
File Dimensione Formato  
2015 Gnavi et al. Mater. Sci. Eng. POST PRINT.pdf

Accesso aperto

Descrizione: Versione finale dell'autore
Tipo di file: POSTPRINT (VERSIONE FINALE DELL’AUTORE)
Dimensione 1.52 MB
Formato Adobe PDF
1.52 MB Adobe PDF Visualizza/Apri
Perroteau_3_167869_The influence.pdf

Accesso riservato

Tipo di file: PDF EDITORIALE
Dimensione 3.22 MB
Formato Adobe PDF
3.22 MB Adobe PDF   Visualizza/Apri   Richiedi una copia

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/2318/151529
Citazioni
  • ???jsp.display-item.citation.pmc??? 21
  • Scopus 60
  • ???jsp.display-item.citation.isi??? 56
social impact