The paper evaluates the effect of the surface treatment on the strength of the single-lap adhesive joints made of the C45 steel. The samples were joined using an adhesive composition consisting of Epidian 57 epoxy resin and PAC curing agent. The study also used Greinplast mosaic plaster with a grain size of 1.0-1.6 mm as coating. The experiment was carried out for 3 variants of joints: sheet/sheet, sheet+plaster/sheet+plaster, sheet/sheet+plaster. Each variant was divided into 3 methods of surface treatment. The strength tests were carried out on the Zwick/Roell Z150 testing machine. The roughness parameters of the surface's samples were measured using a HOMMEL TESTER T1000 profilometer.

The Influence of Technological Factors on the Strength of Adhesive Joints of Steel Sheets

Brunella, V
2020-01-01

Abstract

The paper evaluates the effect of the surface treatment on the strength of the single-lap adhesive joints made of the C45 steel. The samples were joined using an adhesive composition consisting of Epidian 57 epoxy resin and PAC curing agent. The study also used Greinplast mosaic plaster with a grain size of 1.0-1.6 mm as coating. The experiment was carried out for 3 variants of joints: sheet/sheet, sheet+plaster/sheet+plaster, sheet/sheet+plaster. Each variant was divided into 3 methods of surface treatment. The strength tests were carried out on the Zwick/Roell Z150 testing machine. The roughness parameters of the surface's samples were measured using a HOMMEL TESTER T1000 profilometer.
2020
14
1
107
115
adhesive joint; shear strength; surface roughness
Doluk, E; Rudawska, A; Brunella, V
File in questo prodotto:
File Dimensione Formato  
ASTRJ2020_1_107.pdf

Accesso aperto

Descrizione: paper
Tipo di file: PDF EDITORIALE
Dimensione 1.16 MB
Formato Adobe PDF
1.16 MB Adobe PDF Visualizza/Apri

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/2318/1873050
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 4
  • ???jsp.display-item.citation.isi??? 3
social impact