In the present work, we report a preparation strategy for hematite phase-pure photoanodes consisting of Sn-doped hematite nanoflakes/hematite thin film bilayer nanostructure (Sn-HB). This approach is based on a two-step annealing process of pure iron films deposited on fluorine doped tin oxide (FTO) substrates by advanced magnetron sputtering. While the high density hematite ultrathin nanoflakes (HNs) with detrimental iron oxide layers (Fe3O4 and/or FeO) are generated during the first annealing step at 400 degrees C for two hours, the second thermal treatment at 800 degrees C for 15 minutes oxidises all the undesired iron oxide phases to a photoactive hematite layer as well as is providing efficient Sn doping of a drop-casted SnCl4 in order to increase the conductivity. The optimized Sn-HB shows an around 11 times higher photocurrent density (0.71 mA cm(-2) at 1.23 V-RHE) compared with a reference hematite photoanode produced from iron foil under the same conditions.
Magnetite-Free Sn-Doped Hematite Nanoflake Layers for Enhanced Photoelectrochemical Water Splitting
Naldoni, A;
2022-01-01
Abstract
In the present work, we report a preparation strategy for hematite phase-pure photoanodes consisting of Sn-doped hematite nanoflakes/hematite thin film bilayer nanostructure (Sn-HB). This approach is based on a two-step annealing process of pure iron films deposited on fluorine doped tin oxide (FTO) substrates by advanced magnetron sputtering. While the high density hematite ultrathin nanoflakes (HNs) with detrimental iron oxide layers (Fe3O4 and/or FeO) are generated during the first annealing step at 400 degrees C for two hours, the second thermal treatment at 800 degrees C for 15 minutes oxidises all the undesired iron oxide phases to a photoactive hematite layer as well as is providing efficient Sn doping of a drop-casted SnCl4 in order to increase the conductivity. The optimized Sn-HB shows an around 11 times higher photocurrent density (0.71 mA cm(-2) at 1.23 V-RHE) compared with a reference hematite photoanode produced from iron foil under the same conditions.
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.