Anatase and rutile mixed-phase TiO2 with an ideal ratio has been proven to significantly enhance photoelectrochemical (PEC) activity in water-splitting applications due to suppressing the electron-hole recombination. However, the mechanism of this improvement has not been satisfactory described yet. The PEC water oxidation (oxygen evolution) at the interface of TiO2 photoanode and electrolyte solution is determined by the fraction of the photogenerated holes that reach the solution and it is defined as the hole transfer efficiency. The surface and bulk recombination processes in semiconductor photoanodes majorly influence the hole transfer efficiency. In this work, we study the hole transfer process involved in mixed-phase TiO2 nanotube arrays/solution junction using intensity-modulated photocurrent and photovoltage spectroscopy (IMPS and IMVS); then, we correlate the obtained hole transfer rate constants to (photo)electrochemical impedance spectroscopy (PEIS) measurements. The results suggest that the enhanced performance of the TiO2 mixed-phase is due to the improved hole transfer rate across the TiO2/liquid interface as well as to the decrease in the surface trap recombination of the holes.
Radiative and Non-Radiative Recombination Pathways in Mixed-Phase TiO2 Nanotubes for PEC Water-Splitting
Alberto Naldoni
;
2019-01-01
Abstract
Anatase and rutile mixed-phase TiO2 with an ideal ratio has been proven to significantly enhance photoelectrochemical (PEC) activity in water-splitting applications due to suppressing the electron-hole recombination. However, the mechanism of this improvement has not been satisfactory described yet. The PEC water oxidation (oxygen evolution) at the interface of TiO2 photoanode and electrolyte solution is determined by the fraction of the photogenerated holes that reach the solution and it is defined as the hole transfer efficiency. The surface and bulk recombination processes in semiconductor photoanodes majorly influence the hole transfer efficiency. In this work, we study the hole transfer process involved in mixed-phase TiO2 nanotube arrays/solution junction using intensity-modulated photocurrent and photovoltage spectroscopy (IMPS and IMVS); then, we correlate the obtained hole transfer rate constants to (photo)electrochemical impedance spectroscopy (PEIS) measurements. The results suggest that the enhanced performance of the TiO2 mixed-phase is due to the improved hole transfer rate across the TiO2/liquid interface as well as to the decrease in the surface trap recombination of the holes.
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.