The electron-spin-resonance (ESR) features of tetrahedral amorphous carbon (ta-C) samples deposited by S-bend filtered cathodic vacuum arc (FCVA) are investigated in a wide temperature range (4.3–295 K) before and after postdeposition annealing at 500 °C. Special attention is given to the temperature dependence of the linewidths. While the sp3 content does not change with annealing, the temperature trend of the linewidth becomes much smoother for postdeposition annealed samples. The results are discussed in terms of different possible mechanisms of motional line-narrowing and line-narrowing due to hopping motion.
Low temperature investigation of paramagnetic centres in tetrahedral amorphous carbon deposited by S-bend FCVA
LAURENTI, Enzo;
2002-01-01
Abstract
The electron-spin-resonance (ESR) features of tetrahedral amorphous carbon (ta-C) samples deposited by S-bend filtered cathodic vacuum arc (FCVA) are investigated in a wide temperature range (4.3–295 K) before and after postdeposition annealing at 500 °C. Special attention is given to the temperature dependence of the linewidths. While the sp3 content does not change with annealing, the temperature trend of the linewidth becomes much smoother for postdeposition annealed samples. The results are discussed in terms of different possible mechanisms of motional line-narrowing and line-narrowing due to hopping motion.
File in questo prodotto:
Non ci sono file associati a questo prodotto.
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.