Dealumination of NH4-Y zeolite during steaming to 873 K was investigated with in situ, timedependent, synchrotron radiation XRPD and in situ Al K-edge XAS. Water desorption is complete at 450 K, and ammonium decomposition occurs between 500 and 550 K. Only a small fraction of Al3+ species (5%) leaves the framework during heating from 710 to 873 K; these species occupy site I′ inside the sodalite cage. This fraction increases up to 8% in the first 50 min at 873 K and remains constant for the following 70 min isotherm and during the high-temperature part of the cooling experiment. During cooling from 500 to 450 K, the electron density at site I′ increases suddenly, corresponding to a fraction of 30-35% of the total Al, confirmed by ex situ 27Al MAS solid-state NMR. At that temperature, in situ Al K-edge XAS indicates a change in Al coordination of a large fraction of Al, and thermogravimetric (TG) data show the first water molecules start to repopulate the pores. Such molecules drive the dislodgment of most of the Al from the zeolitic framework. Our data indicate that considerable structural collapse caused by steaming does not occur at the highest temperature; however, defects form, which lead to significant migration of framework Al3+ to extraframework positions, which occurs only as water is able to enter the pores again, that is, at much lower temperature. Contrary to general opinion, these results demonstrate that zeolite dealumination is not primarily a high-temperature process. The standard Rietveld refinement approach failed to identify extraframework Al species. These new results were obtained by adopting the innovative parametric refinement [J. Appl. Crystallogr. 2007, 40, 87]. Treating all of the XRPD patterns collected during the evolution of temperature as one unique data set significantly reduces the overall number of optimized variables and, thus, their relative correlation, and finally results in a more reliable estimate of the optimized parameters. Our results contribute to a better understanding of the Phenomena involved on the atomic scale in the preparation of ultrastable Y zeolites (USY). USY are employed in fluid catalytic cracking (FCC), which is the most important conversion process in petroleum refineries to convert the high-boiling hydrocarbon fractions of petroleum crude oils to more valuable products like gasoline and olefinic gases
In Situ XAS and XRPD Parametric Rietveld Refinement To Understand Dealumination of Y Zeolite Catalyst
AGOSTINI, Giovanni;LAMBERTI, Carlo;
2010-01-01
Abstract
Dealumination of NH4-Y zeolite during steaming to 873 K was investigated with in situ, timedependent, synchrotron radiation XRPD and in situ Al K-edge XAS. Water desorption is complete at 450 K, and ammonium decomposition occurs between 500 and 550 K. Only a small fraction of Al3+ species (5%) leaves the framework during heating from 710 to 873 K; these species occupy site I′ inside the sodalite cage. This fraction increases up to 8% in the first 50 min at 873 K and remains constant for the following 70 min isotherm and during the high-temperature part of the cooling experiment. During cooling from 500 to 450 K, the electron density at site I′ increases suddenly, corresponding to a fraction of 30-35% of the total Al, confirmed by ex situ 27Al MAS solid-state NMR. At that temperature, in situ Al K-edge XAS indicates a change in Al coordination of a large fraction of Al, and thermogravimetric (TG) data show the first water molecules start to repopulate the pores. Such molecules drive the dislodgment of most of the Al from the zeolitic framework. Our data indicate that considerable structural collapse caused by steaming does not occur at the highest temperature; however, defects form, which lead to significant migration of framework Al3+ to extraframework positions, which occurs only as water is able to enter the pores again, that is, at much lower temperature. Contrary to general opinion, these results demonstrate that zeolite dealumination is not primarily a high-temperature process. The standard Rietveld refinement approach failed to identify extraframework Al species. These new results were obtained by adopting the innovative parametric refinement [J. Appl. Crystallogr. 2007, 40, 87]. Treating all of the XRPD patterns collected during the evolution of temperature as one unique data set significantly reduces the overall number of optimized variables and, thus, their relative correlation, and finally results in a more reliable estimate of the optimized parameters. Our results contribute to a better understanding of the Phenomena involved on the atomic scale in the preparation of ultrastable Y zeolites (USY). USY are employed in fluid catalytic cracking (FCC), which is the most important conversion process in petroleum refineries to convert the high-boiling hydrocarbon fractions of petroleum crude oils to more valuable products like gasoline and olefinic gases
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.